Preparation and characterization of the spinel series Co6+xNi4-xMn8O24 (0≤x≤4)
Identifieur interne : 000289 ( PascalFrancis/Corpus ); précédent : 000288; suivant : 000290Preparation and characterization of the spinel series Co6+xNi4-xMn8O24 (0≤x≤4)
Auteurs : C. Boudaya ; L. Laroussi ; E. Dhahri ; J. C. Joubert ; A. Cheikh-RouhouSource :
- Phase transitions : (Print) [ 0141-1594 ] ; 1999.
Descripteurs français
- Pascal (Inist)
English descriptors
- KwdEn :
Abstract
Samples of the spinel series, Co6+xNi4-xMn8O24 (0≤x≤4), prepared by traditional ceramic procedures, are characterized by X-ray diffraction, SEM techniques and magnetization measurements. In the whole concentration range, a single-phase cubic spinels are obtained at a sintering temperature of 1050°C for a period of time of 72 h. SEM analysis showed that the ceramics are well densified and consisted of well individualized grains of a narrow size distribution. Magnetization measurements revealed the existence of a Yafet-Kittel configuration at low temperature and a ferrimagnetic-paramagnetic transition with increasing temperature. The Curie temperature decreased from 250 K for x = 2.5 to 200 K for x = 4.
Notice en format standard (ISO 2709)
Pour connaître la documentation sur le format Inist Standard.
pA |
|
---|
Format Inist (serveur)
NO : | PASCAL 00-0244953 INIST |
---|---|
ET : | Preparation and characterization of the spinel series Co6+xNi4-xMn8O24 (0≤x≤4) |
AU : | BOUDAYA (C.); LAROUSSI (L.); DHAHRI (E.); JOUBERT (J. C.); CHEIKH-ROUHOU (A.) |
AF : | Laboratoire de Physique des matériaux, Faculté des Sciences de Sfax, BP 763/3038 Sfax/Tunisie (1 aut., 2 aut., 3 aut., 5 aut.); Laboratoire des Matériaux et de Génie Physique, CNRS UMR 5628, ENSPG, BP 46/38402 Saint Martin d'Hères/France (4 aut.) |
DT : | Publication en série; Niveau analytique |
SO : | Phase transitions : (Print); ISSN 0141-1594; Coden PHTRDP; Suisse; Da. 1999; Vol. 68; No. 4 SEC.A; Pp. 631-642; Bibl. 6 ref. |
LA : | Anglais |
EA : | Samples of the spinel series, Co6+xNi4-xMn8O24 (0≤x≤4), prepared by traditional ceramic procedures, are characterized by X-ray diffraction, SEM techniques and magnetization measurements. In the whole concentration range, a single-phase cubic spinels are obtained at a sintering temperature of 1050°C for a period of time of 72 h. SEM analysis showed that the ceramics are well densified and consisted of well individualized grains of a narrow size distribution. Magnetization measurements revealed the existence of a Yafet-Kittel configuration at low temperature and a ferrimagnetic-paramagnetic transition with increasing temperature. The Curie temperature decreased from 250 K for x = 2.5 to 200 K for x = 4. |
CC : | 001B60A66F1; 001B70E30K |
FD : | Etude expérimentale; Préparation; Frittage; Microstructure; Structure cristalline; Aimantation; Point Curie; Transition magnétique; Effet concentration; Diffraction RX; SEM; Spinelles; Cobalt oxyde; Nickel oxyde; Manganèse oxyde; Composé quaternaire; Co6+xNi4-xMn8O24; Co Mn Ni O; 6166F; 7530K |
FG : | Composé minéral; Métal transition composé |
ED : | Experimental study; Preparation; Sintering; Microstructure; Crystal structure; Magnetization; Curie point; Magnetic transitions; Quantity ratio; XRD; SEM; Spinels; Cobalt oxides; Nickel oxides; Manganese oxides; Quaternary compounds |
EG : | Inorganic compounds; Transition element compounds |
SD : | Preparación |
LO : | INIST-18257.354000087219130040 |
ID : | 00-0244953 |
Links to Exploration step
Pascal:00-0244953Le document en format XML
<record><TEI><teiHeader><fileDesc><titleStmt><title xml:lang="en" level="a">Preparation and characterization of the spinel series Co<sub>6+x</sub>
Ni<sub>4-x</sub>
Mn<sub>8</sub>
O<sub>24</sub>
(0≤x≤4)</title>
<author><name sortKey="Boudaya, C" sort="Boudaya, C" uniqKey="Boudaya C" first="C." last="Boudaya">C. Boudaya</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire de Physique des matériaux, Faculté des Sciences de Sfax, BP 763</s1>
<s2>3038 Sfax</s2>
<s3>TUN</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Laroussi, L" sort="Laroussi, L" uniqKey="Laroussi L" first="L." last="Laroussi">L. Laroussi</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire de Physique des matériaux, Faculté des Sciences de Sfax, BP 763</s1>
<s2>3038 Sfax</s2>
<s3>TUN</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Dhahri, E" sort="Dhahri, E" uniqKey="Dhahri E" first="E." last="Dhahri">E. Dhahri</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire de Physique des matériaux, Faculté des Sciences de Sfax, BP 763</s1>
<s2>3038 Sfax</s2>
<s3>TUN</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Joubert, J C" sort="Joubert, J C" uniqKey="Joubert J" first="J. C." last="Joubert">J. C. Joubert</name>
<affiliation><inist:fA14 i1="02"><s1>Laboratoire des Matériaux et de Génie Physique, CNRS UMR 5628, ENSPG, BP 46</s1>
<s2>38402 Saint Martin d'Hères</s2>
<s3>FRA</s3>
<sZ>4 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Cheikh Rouhou, A" sort="Cheikh Rouhou, A" uniqKey="Cheikh Rouhou A" first="A." last="Cheikh-Rouhou">A. Cheikh-Rouhou</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire de Physique des matériaux, Faculté des Sciences de Sfax, BP 763</s1>
<s2>3038 Sfax</s2>
<s3>TUN</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
</titleStmt>
<publicationStmt><idno type="wicri:source">INIST</idno>
<idno type="inist">00-0244953</idno>
<date when="1999">1999</date>
<idno type="stanalyst">PASCAL 00-0244953 INIST</idno>
<idno type="RBID">Pascal:00-0244953</idno>
<idno type="wicri:Area/PascalFrancis/Corpus">000289</idno>
</publicationStmt>
<sourceDesc><biblStruct><analytic><title xml:lang="en" level="a">Preparation and characterization of the spinel series Co<sub>6+x</sub>
Ni<sub>4-x</sub>
Mn<sub>8</sub>
O<sub>24</sub>
(0≤x≤4)</title>
<author><name sortKey="Boudaya, C" sort="Boudaya, C" uniqKey="Boudaya C" first="C." last="Boudaya">C. Boudaya</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire de Physique des matériaux, Faculté des Sciences de Sfax, BP 763</s1>
<s2>3038 Sfax</s2>
<s3>TUN</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Laroussi, L" sort="Laroussi, L" uniqKey="Laroussi L" first="L." last="Laroussi">L. Laroussi</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire de Physique des matériaux, Faculté des Sciences de Sfax, BP 763</s1>
<s2>3038 Sfax</s2>
<s3>TUN</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Dhahri, E" sort="Dhahri, E" uniqKey="Dhahri E" first="E." last="Dhahri">E. Dhahri</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire de Physique des matériaux, Faculté des Sciences de Sfax, BP 763</s1>
<s2>3038 Sfax</s2>
<s3>TUN</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Joubert, J C" sort="Joubert, J C" uniqKey="Joubert J" first="J. C." last="Joubert">J. C. Joubert</name>
<affiliation><inist:fA14 i1="02"><s1>Laboratoire des Matériaux et de Génie Physique, CNRS UMR 5628, ENSPG, BP 46</s1>
<s2>38402 Saint Martin d'Hères</s2>
<s3>FRA</s3>
<sZ>4 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Cheikh Rouhou, A" sort="Cheikh Rouhou, A" uniqKey="Cheikh Rouhou A" first="A." last="Cheikh-Rouhou">A. Cheikh-Rouhou</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire de Physique des matériaux, Faculté des Sciences de Sfax, BP 763</s1>
<s2>3038 Sfax</s2>
<s3>TUN</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
</analytic>
<series><title level="j" type="main">Phase transitions : (Print)</title>
<title level="j" type="abbreviated">Phase transit. : (Print)</title>
<idno type="ISSN">0141-1594</idno>
<imprint><date when="1999">1999</date>
</imprint>
</series>
</biblStruct>
</sourceDesc>
<seriesStmt><title level="j" type="main">Phase transitions : (Print)</title>
<title level="j" type="abbreviated">Phase transit. : (Print)</title>
<idno type="ISSN">0141-1594</idno>
</seriesStmt>
</fileDesc>
<profileDesc><textClass><keywords scheme="KwdEn" xml:lang="en"><term>Cobalt oxides</term>
<term>Crystal structure</term>
<term>Curie point</term>
<term>Experimental study</term>
<term>Magnetic transitions</term>
<term>Magnetization</term>
<term>Manganese oxides</term>
<term>Microstructure</term>
<term>Nickel oxides</term>
<term>Preparation</term>
<term>Quantity ratio</term>
<term>Quaternary compounds</term>
<term>SEM</term>
<term>Sintering</term>
<term>Spinels</term>
<term>XRD</term>
</keywords>
<keywords scheme="Pascal" xml:lang="fr"><term>Etude expérimentale</term>
<term>Préparation</term>
<term>Frittage</term>
<term>Microstructure</term>
<term>Structure cristalline</term>
<term>Aimantation</term>
<term>Point Curie</term>
<term>Transition magnétique</term>
<term>Effet concentration</term>
<term>Diffraction RX</term>
<term>SEM</term>
<term>Spinelles</term>
<term>Cobalt oxyde</term>
<term>Nickel oxyde</term>
<term>Manganèse oxyde</term>
<term>Composé quaternaire</term>
<term>Co6+xNi4-xMn8O24</term>
<term>Co Mn Ni O</term>
<term>6166F</term>
<term>7530K</term>
</keywords>
</textClass>
</profileDesc>
</teiHeader>
<front><div type="abstract" xml:lang="en">Samples of the spinel series, Co<sub>6+x</sub>
Ni<sub>4-x</sub>
Mn<sub>8</sub>
O<sub>24</sub>
(0≤x≤4), prepared by traditional ceramic procedures, are characterized by X-ray diffraction, SEM techniques and magnetization measurements. In the whole concentration range, a single-phase cubic spinels are obtained at a sintering temperature of 1050°C for a period of time of 72 h. SEM analysis showed that the ceramics are well densified and consisted of well individualized grains of a narrow size distribution. Magnetization measurements revealed the existence of a Yafet-Kittel configuration at low temperature and a ferrimagnetic-paramagnetic transition with increasing temperature. The Curie temperature decreased from 250 K for x = 2.5 to 200 K for x = 4.</div>
</front>
</TEI>
<inist><standard h6="B"><pA><fA01 i1="01" i2="1"><s0>0141-1594</s0>
</fA01>
<fA02 i1="01"><s0>PHTRDP</s0>
</fA02>
<fA03 i2="1"><s0>Phase transit. : (Print)</s0>
</fA03>
<fA05><s2>68</s2>
</fA05>
<fA06><s2>4</s2>
<s3>SEC.A</s3>
</fA06>
<fA08 i1="01" i2="1" l="ENG"><s1>Preparation and characterization of the spinel series Co<sub>6+x</sub>
Ni<sub>4-x</sub>
Mn<sub>8</sub>
O<sub>24</sub>
(0≤x≤4)</s1>
</fA08>
<fA11 i1="01" i2="1"><s1>BOUDAYA (C.)</s1>
</fA11>
<fA11 i1="02" i2="1"><s1>LAROUSSI (L.)</s1>
</fA11>
<fA11 i1="03" i2="1"><s1>DHAHRI (E.)</s1>
</fA11>
<fA11 i1="04" i2="1"><s1>JOUBERT (J. C.)</s1>
</fA11>
<fA11 i1="05" i2="1"><s1>CHEIKH-ROUHOU (A.)</s1>
</fA11>
<fA14 i1="01"><s1>Laboratoire de Physique des matériaux, Faculté des Sciences de Sfax, BP 763</s1>
<s2>3038 Sfax</s2>
<s3>TUN</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</fA14>
<fA14 i1="02"><s1>Laboratoire des Matériaux et de Génie Physique, CNRS UMR 5628, ENSPG, BP 46</s1>
<s2>38402 Saint Martin d'Hères</s2>
<s3>FRA</s3>
<sZ>4 aut.</sZ>
</fA14>
<fA20><s1>631-642</s1>
</fA20>
<fA21><s1>1999</s1>
</fA21>
<fA23 i1="01"><s0>ENG</s0>
</fA23>
<fA43 i1="01"><s1>INIST</s1>
<s2>18257</s2>
<s5>354000087219130040</s5>
</fA43>
<fA44><s0>0000</s0>
<s1>© 2000 INIST-CNRS. All rights reserved.</s1>
</fA44>
<fA45><s0>6 ref.</s0>
</fA45>
<fA47 i1="01" i2="1"><s0>00-0244953</s0>
</fA47>
<fA60><s1>P</s1>
</fA60>
<fA61><s0>A</s0>
</fA61>
<fA64 i1="01" i2="1"><s0>Phase transitions : (Print)</s0>
</fA64>
<fA66 i1="01"><s0>CHE</s0>
</fA66>
<fC01 i1="01" l="ENG"><s0>Samples of the spinel series, Co<sub>6+x</sub>
Ni<sub>4-x</sub>
Mn<sub>8</sub>
O<sub>24</sub>
(0≤x≤4), prepared by traditional ceramic procedures, are characterized by X-ray diffraction, SEM techniques and magnetization measurements. In the whole concentration range, a single-phase cubic spinels are obtained at a sintering temperature of 1050°C for a period of time of 72 h. SEM analysis showed that the ceramics are well densified and consisted of well individualized grains of a narrow size distribution. Magnetization measurements revealed the existence of a Yafet-Kittel configuration at low temperature and a ferrimagnetic-paramagnetic transition with increasing temperature. The Curie temperature decreased from 250 K for x = 2.5 to 200 K for x = 4.</s0>
</fC01>
<fC02 i1="01" i2="3"><s0>001B60A66F1</s0>
</fC02>
<fC02 i1="02" i2="3"><s0>001B70E30K</s0>
</fC02>
<fC03 i1="01" i2="3" l="FRE"><s0>Etude expérimentale</s0>
<s5>01</s5>
</fC03>
<fC03 i1="01" i2="3" l="ENG"><s0>Experimental study</s0>
<s5>01</s5>
</fC03>
<fC03 i1="02" i2="X" l="FRE"><s0>Préparation</s0>
<s5>02</s5>
</fC03>
<fC03 i1="02" i2="X" l="ENG"><s0>Preparation</s0>
<s5>02</s5>
</fC03>
<fC03 i1="02" i2="X" l="SPA"><s0>Preparación</s0>
<s5>02</s5>
</fC03>
<fC03 i1="03" i2="3" l="FRE"><s0>Frittage</s0>
<s5>03</s5>
</fC03>
<fC03 i1="03" i2="3" l="ENG"><s0>Sintering</s0>
<s5>03</s5>
</fC03>
<fC03 i1="04" i2="3" l="FRE"><s0>Microstructure</s0>
<s5>04</s5>
</fC03>
<fC03 i1="04" i2="3" l="ENG"><s0>Microstructure</s0>
<s5>04</s5>
</fC03>
<fC03 i1="05" i2="3" l="FRE"><s0>Structure cristalline</s0>
<s5>05</s5>
</fC03>
<fC03 i1="05" i2="3" l="ENG"><s0>Crystal structure</s0>
<s5>05</s5>
</fC03>
<fC03 i1="06" i2="3" l="FRE"><s0>Aimantation</s0>
<s5>06</s5>
</fC03>
<fC03 i1="06" i2="3" l="ENG"><s0>Magnetization</s0>
<s5>06</s5>
</fC03>
<fC03 i1="07" i2="3" l="FRE"><s0>Point Curie</s0>
<s5>07</s5>
</fC03>
<fC03 i1="07" i2="3" l="ENG"><s0>Curie point</s0>
<s5>07</s5>
</fC03>
<fC03 i1="08" i2="3" l="FRE"><s0>Transition magnétique</s0>
<s5>08</s5>
</fC03>
<fC03 i1="08" i2="3" l="ENG"><s0>Magnetic transitions</s0>
<s5>08</s5>
</fC03>
<fC03 i1="09" i2="3" l="FRE"><s0>Effet concentration</s0>
<s5>11</s5>
</fC03>
<fC03 i1="09" i2="3" l="ENG"><s0>Quantity ratio</s0>
<s5>11</s5>
</fC03>
<fC03 i1="10" i2="3" l="FRE"><s0>Diffraction RX</s0>
<s5>12</s5>
</fC03>
<fC03 i1="10" i2="3" l="ENG"><s0>XRD</s0>
<s5>12</s5>
</fC03>
<fC03 i1="11" i2="3" l="FRE"><s0>SEM</s0>
<s5>13</s5>
</fC03>
<fC03 i1="11" i2="3" l="ENG"><s0>SEM</s0>
<s5>13</s5>
</fC03>
<fC03 i1="12" i2="3" l="FRE"><s0>Spinelles</s0>
<s5>15</s5>
</fC03>
<fC03 i1="12" i2="3" l="ENG"><s0>Spinels</s0>
<s5>15</s5>
</fC03>
<fC03 i1="13" i2="3" l="FRE"><s0>Cobalt oxyde</s0>
<s2>NK</s2>
<s5>16</s5>
</fC03>
<fC03 i1="13" i2="3" l="ENG"><s0>Cobalt oxides</s0>
<s2>NK</s2>
<s5>16</s5>
</fC03>
<fC03 i1="14" i2="3" l="FRE"><s0>Nickel oxyde</s0>
<s2>NK</s2>
<s5>17</s5>
</fC03>
<fC03 i1="14" i2="3" l="ENG"><s0>Nickel oxides</s0>
<s2>NK</s2>
<s5>17</s5>
</fC03>
<fC03 i1="15" i2="3" l="FRE"><s0>Manganèse oxyde</s0>
<s2>NK</s2>
<s5>18</s5>
</fC03>
<fC03 i1="15" i2="3" l="ENG"><s0>Manganese oxides</s0>
<s2>NK</s2>
<s5>18</s5>
</fC03>
<fC03 i1="16" i2="3" l="FRE"><s0>Composé quaternaire</s0>
<s5>19</s5>
</fC03>
<fC03 i1="16" i2="3" l="ENG"><s0>Quaternary compounds</s0>
<s5>19</s5>
</fC03>
<fC03 i1="17" i2="3" l="FRE"><s0>Co6+xNi4-xMn8O24</s0>
<s4>INC</s4>
<s5>52</s5>
</fC03>
<fC03 i1="18" i2="3" l="FRE"><s0>Co Mn Ni O</s0>
<s4>INC</s4>
<s5>53</s5>
</fC03>
<fC03 i1="19" i2="3" l="FRE"><s0>6166F</s0>
<s2>PAC</s2>
<s4>INC</s4>
<s5>56</s5>
</fC03>
<fC03 i1="20" i2="3" l="FRE"><s0>7530K</s0>
<s2>PAC</s2>
<s4>INC</s4>
<s5>57</s5>
</fC03>
<fC07 i1="01" i2="3" l="FRE"><s0>Composé minéral</s0>
<s5>48</s5>
</fC07>
<fC07 i1="01" i2="3" l="ENG"><s0>Inorganic compounds</s0>
<s5>48</s5>
</fC07>
<fC07 i1="02" i2="3" l="FRE"><s0>Métal transition composé</s0>
<s5>49</s5>
</fC07>
<fC07 i1="02" i2="3" l="ENG"><s0>Transition element compounds</s0>
<s5>49</s5>
</fC07>
<fN21><s1>164</s1>
</fN21>
</pA>
</standard>
<server><NO>PASCAL 00-0244953 INIST</NO>
<ET>Preparation and characterization of the spinel series Co<sub>6+x</sub>
Ni<sub>4-x</sub>
Mn<sub>8</sub>
O<sub>24</sub>
(0≤x≤4)</ET>
<AU>BOUDAYA (C.); LAROUSSI (L.); DHAHRI (E.); JOUBERT (J. C.); CHEIKH-ROUHOU (A.)</AU>
<AF>Laboratoire de Physique des matériaux, Faculté des Sciences de Sfax, BP 763/3038 Sfax/Tunisie (1 aut., 2 aut., 3 aut., 5 aut.); Laboratoire des Matériaux et de Génie Physique, CNRS UMR 5628, ENSPG, BP 46/38402 Saint Martin d'Hères/France (4 aut.)</AF>
<DT>Publication en série; Niveau analytique</DT>
<SO>Phase transitions : (Print); ISSN 0141-1594; Coden PHTRDP; Suisse; Da. 1999; Vol. 68; No. 4 SEC.A; Pp. 631-642; Bibl. 6 ref.</SO>
<LA>Anglais</LA>
<EA>Samples of the spinel series, Co<sub>6+x</sub>
Ni<sub>4-x</sub>
Mn<sub>8</sub>
O<sub>24</sub>
(0≤x≤4), prepared by traditional ceramic procedures, are characterized by X-ray diffraction, SEM techniques and magnetization measurements. In the whole concentration range, a single-phase cubic spinels are obtained at a sintering temperature of 1050°C for a period of time of 72 h. SEM analysis showed that the ceramics are well densified and consisted of well individualized grains of a narrow size distribution. Magnetization measurements revealed the existence of a Yafet-Kittel configuration at low temperature and a ferrimagnetic-paramagnetic transition with increasing temperature. The Curie temperature decreased from 250 K for x = 2.5 to 200 K for x = 4.</EA>
<CC>001B60A66F1; 001B70E30K</CC>
<FD>Etude expérimentale; Préparation; Frittage; Microstructure; Structure cristalline; Aimantation; Point Curie; Transition magnétique; Effet concentration; Diffraction RX; SEM; Spinelles; Cobalt oxyde; Nickel oxyde; Manganèse oxyde; Composé quaternaire; Co6+xNi4-xMn8O24; Co Mn Ni O; 6166F; 7530K</FD>
<FG>Composé minéral; Métal transition composé</FG>
<ED>Experimental study; Preparation; Sintering; Microstructure; Crystal structure; Magnetization; Curie point; Magnetic transitions; Quantity ratio; XRD; SEM; Spinels; Cobalt oxides; Nickel oxides; Manganese oxides; Quaternary compounds</ED>
<EG>Inorganic compounds; Transition element compounds</EG>
<SD>Preparación</SD>
<LO>INIST-18257.354000087219130040</LO>
<ID>00-0244953</ID>
</server>
</inist>
</record>
Pour manipuler ce document sous Unix (Dilib)
EXPLOR_STEP=$WICRI_ROOT/Wicri/Terre/explor/CobaltMaghrebV1/Data/PascalFrancis/Corpus
HfdSelect -h $EXPLOR_STEP/biblio.hfd -nk 000289 | SxmlIndent | more
Ou
HfdSelect -h $EXPLOR_AREA/Data/PascalFrancis/Corpus/biblio.hfd -nk 000289 | SxmlIndent | more
Pour mettre un lien sur cette page dans le réseau Wicri
{{Explor lien |wiki= Wicri/Terre |area= CobaltMaghrebV1 |flux= PascalFrancis |étape= Corpus |type= RBID |clé= Pascal:00-0244953 |texte= Preparation and characterization of the spinel series Co6+xNi4-xMn8O24 (0≤x≤4) }}
This area was generated with Dilib version V0.6.32. |