Template synthesis of carbon nanotubes
Identifieur interne : 000D82 ( Main/Exploration ); précédent : 000D81; suivant : 000D83Template synthesis of carbon nanotubes
Auteurs : G. L. Hornyak [États-Unis] ; A. C. Dillon [États-Unis] ; P. A. Parilla [États-Unis] ; J. J. Schneider [Allemagne] ; N. Czap [Allemagne] ; K. M. Jones [États-Unis] ; F. S. Fasoon [États-Unis] ; A. Mason [États-Unis] ; M. J. Heben [États-Unis]Source :
- Nanostructured Materials [ 0965-9773 ] ; 1999.
Abstract
Abstract: The template synthesis and characterization of carbon nanotubes (CNTs) formed in porous alumina membranes (PAM) by the thermal chemical vapor decomposition (CVD) of propylene (Pr) gas are described. We found that the graphitic character of CNTs improved as CVD temperature was increased from 500 to 800 °C. Samples showed progressive increases in metallic appearance and layered tube wall structure and decreases in electrical resistance. No further enhancement of graphitization was observed among samples formed at 800, 900 and 1000 °C. X-ray diffraction (XRD) indicated that long-range order was absent in all CNTs tested. Localized crystalline domains of graphitic carbon, however, were detected by Roman spectroscopy and seen in light and dark field transmission electron microscopy (TEM) images. CNTs formed in the presence of catalytic Fe and Co particles at 600 and 700 °C with a Pr/N2 flow rate of 94 sccm (standard cubic centimeters per minute) showed slightly lower electrical resistance than CNTs formed in control experiments. The catalytic effects of Fe and Co were observed for samples made at 800 °C with a 50 sccm Pr/N2 flow rate as “nanotubes within nanotubes” were formed. No major differences were found between catalyst-containing and control samples formed at temperatures greater than or equal to 800 °C at 94 sccm.
Url:
DOI: 10.1016/S0965-9773(99)00071-9
Affiliations:
Links toward previous steps (curation, corpus...)
- to stream Istex, to step Corpus: 000C39
- to stream Istex, to step Curation: 000821
- to stream Istex, to step Checkpoint: 000678
- to stream Main, to step Merge: 000E10
- to stream Main, to step Curation: 000D82
Le document en format XML
<record><TEI wicri:istexFullTextTei="biblStruct"><teiHeader><fileDesc><titleStmt><title xml:lang="en">Template synthesis of carbon nanotubes</title><author><name sortKey="Hornyak, G L" sort="Hornyak, G L" uniqKey="Hornyak G" first="G. L." last="Hornyak">G. L. Hornyak</name></author><author><name sortKey="Dillon, A C" sort="Dillon, A C" uniqKey="Dillon A" first="A. C." last="Dillon">A. C. Dillon</name></author><author><name sortKey="Parilla, P A" sort="Parilla, P A" uniqKey="Parilla P" first="P. A." last="Parilla">P. A. Parilla</name></author><author><name sortKey="Schneider, J J" sort="Schneider, J J" uniqKey="Schneider J" first="J. J." last="Schneider">J. J. Schneider</name></author><author><name sortKey="Czap, N" sort="Czap, N" uniqKey="Czap N" first="N." last="Czap">N. Czap</name></author><author><name sortKey="Jones, K M" sort="Jones, K M" uniqKey="Jones K" first="K. M." last="Jones">K. M. Jones</name></author><author><name sortKey="Fasoon, F S" sort="Fasoon, F S" uniqKey="Fasoon F" first="F. S." last="Fasoon">F. S. Fasoon</name></author><author><name sortKey="Mason, A" sort="Mason, A" uniqKey="Mason A" first="A." last="Mason">A. Mason</name></author><author><name sortKey="Heben, M J" sort="Heben, M J" uniqKey="Heben M" first="M. J." last="Heben">M. J. Heben</name></author></titleStmt><publicationStmt><idno type="wicri:source">ISTEX</idno><idno type="RBID">ISTEX:DFCCF840DD830F7B0FE1317D587FA0B9FBF5A8D1</idno><date when="1999" year="1999">1999</date><idno type="doi">10.1016/S0965-9773(99)00071-9</idno><idno type="url">https://api.istex.fr/document/DFCCF840DD830F7B0FE1317D587FA0B9FBF5A8D1/fulltext/pdf</idno><idno type="wicri:Area/Istex/Corpus">000C39</idno><idno type="wicri:explorRef" wicri:stream="Istex" wicri:step="Corpus" wicri:corpus="ISTEX">000C39</idno><idno type="wicri:Area/Istex/Curation">000821</idno><idno type="wicri:Area/Istex/Checkpoint">000678</idno><idno type="wicri:explorRef" wicri:stream="Istex" wicri:step="Checkpoint">000678</idno><idno type="wicri:doubleKey">0965-9773:1999:Hornyak G:template:synthesis:of</idno><idno type="wicri:Area/Main/Merge">000E10</idno><idno type="wicri:Area/Main/Curation">000D82</idno><idno type="wicri:Area/Main/Exploration">000D82</idno></publicationStmt><sourceDesc><biblStruct><analytic><title level="a" type="main" xml:lang="en">Template synthesis of carbon nanotubes</title><author><name sortKey="Hornyak, G L" sort="Hornyak, G L" uniqKey="Hornyak G" first="G. L." last="Hornyak">G. L. Hornyak</name><affiliation wicri:level="2"><country xml:lang="fr">États-Unis</country><placeName><region type="state">Colorado</region></placeName><wicri:cityArea>National Renewable Energy Laboratory 1617 Cole Blvd., Golden</wicri:cityArea></affiliation></author><author><name sortKey="Dillon, A C" sort="Dillon, A C" uniqKey="Dillon A" first="A. C." last="Dillon">A. C. Dillon</name><affiliation wicri:level="2"><country xml:lang="fr">États-Unis</country><placeName><region type="state">Colorado</region></placeName><wicri:cityArea>National Renewable Energy Laboratory 1617 Cole Blvd., Golden</wicri:cityArea></affiliation></author><author><name sortKey="Parilla, P A" sort="Parilla, P A" uniqKey="Parilla P" first="P. A." last="Parilla">P. A. Parilla</name><affiliation wicri:level="2"><country xml:lang="fr">États-Unis</country><placeName><region type="state">Colorado</region></placeName><wicri:cityArea>National Renewable Energy Laboratory 1617 Cole Blvd., Golden</wicri:cityArea></affiliation></author><author><name sortKey="Schneider, J J" sort="Schneider, J J" uniqKey="Schneider J" first="J. J." last="Schneider">J. J. Schneider</name><affiliation wicri:level="1"><country xml:lang="fr">Allemagne</country><wicri:regionArea>Institut für Anorganische Chemie, Universität Essen, 45117 Essen</wicri:regionArea><wicri:noRegion>45117 Essen</wicri:noRegion><wicri:noRegion>45117 Essen</wicri:noRegion></affiliation></author><author><name sortKey="Czap, N" sort="Czap, N" uniqKey="Czap N" first="N." last="Czap">N. Czap</name><affiliation wicri:level="1"><country xml:lang="fr">Allemagne</country><wicri:regionArea>Institut für Anorganische Chemie, Universität Essen, 45117 Essen</wicri:regionArea><wicri:noRegion>45117 Essen</wicri:noRegion><wicri:noRegion>45117 Essen</wicri:noRegion></affiliation></author><author><name sortKey="Jones, K M" sort="Jones, K M" uniqKey="Jones K" first="K. M." last="Jones">K. M. Jones</name><affiliation wicri:level="2"><country xml:lang="fr">États-Unis</country><placeName><region type="state">Colorado</region></placeName><wicri:cityArea>National Renewable Energy Laboratory 1617 Cole Blvd., Golden</wicri:cityArea></affiliation></author><author><name sortKey="Fasoon, F S" sort="Fasoon, F S" uniqKey="Fasoon F" first="F. S." last="Fasoon">F. S. Fasoon</name><affiliation wicri:level="2"><country xml:lang="fr">États-Unis</country><placeName><region type="state">Colorado</region></placeName><wicri:cityArea>National Renewable Energy Laboratory 1617 Cole Blvd., Golden</wicri:cityArea></affiliation></author><author><name sortKey="Mason, A" sort="Mason, A" uniqKey="Mason A" first="A." last="Mason">A. Mason</name><affiliation wicri:level="2"><country xml:lang="fr">États-Unis</country><placeName><region type="state">Colorado</region></placeName><wicri:cityArea>National Renewable Energy Laboratory 1617 Cole Blvd., Golden</wicri:cityArea></affiliation></author><author><name sortKey="Heben, M J" sort="Heben, M J" uniqKey="Heben M" first="M. J." last="Heben">M. J. Heben</name><affiliation wicri:level="2"><country xml:lang="fr">États-Unis</country><placeName><region type="state">Colorado</region></placeName><wicri:cityArea>National Renewable Energy Laboratory 1617 Cole Blvd., Golden</wicri:cityArea></affiliation></author></analytic><monogr></monogr><series><title level="j">Nanostructured Materials</title><title level="j" type="abbrev">NM</title><idno type="ISSN">0965-9773</idno><imprint><publisher>ELSEVIER</publisher><date type="published" when="1999">1999</date><biblScope unit="volume">12</biblScope><biblScope unit="issue">1–4</biblScope><biblScope unit="page" from="83">83</biblScope><biblScope unit="page" to="88">88</biblScope></imprint><idno type="ISSN">0965-9773</idno></series><idno type="istex">DFCCF840DD830F7B0FE1317D587FA0B9FBF5A8D1</idno><idno type="DOI">10.1016/S0965-9773(99)00071-9</idno><idno type="PII">S0965-9773(99)00071-9</idno><idno type="ArticleID">99000719</idno></biblStruct></sourceDesc><seriesStmt><idno type="ISSN">0965-9773</idno></seriesStmt></fileDesc><profileDesc><textClass></textClass><langUsage><language ident="en">en</language></langUsage></profileDesc></teiHeader><front><div type="abstract" xml:lang="en">Abstract: The template synthesis and characterization of carbon nanotubes (CNTs) formed in porous alumina membranes (PAM) by the thermal chemical vapor decomposition (CVD) of propylene (Pr) gas are described. We found that the graphitic character of CNTs improved as CVD temperature was increased from 500 to 800 °C. Samples showed progressive increases in metallic appearance and layered tube wall structure and decreases in electrical resistance. No further enhancement of graphitization was observed among samples formed at 800, 900 and 1000 °C. X-ray diffraction (XRD) indicated that long-range order was absent in all CNTs tested. Localized crystalline domains of graphitic carbon, however, were detected by Roman spectroscopy and seen in light and dark field transmission electron microscopy (TEM) images. CNTs formed in the presence of catalytic Fe and Co particles at 600 and 700 °C with a Pr/N2 flow rate of 94 sccm (standard cubic centimeters per minute) showed slightly lower electrical resistance than CNTs formed in control experiments. The catalytic effects of Fe and Co were observed for samples made at 800 °C with a 50 sccm Pr/N2 flow rate as “nanotubes within nanotubes” were formed. No major differences were found between catalyst-containing and control samples formed at temperatures greater than or equal to 800 °C at 94 sccm.</div></front></TEI><affiliations><list><country><li>Allemagne</li><li>États-Unis</li></country><region><li>Colorado</li></region></list><tree><country name="États-Unis"><region name="Colorado"><name sortKey="Hornyak, G L" sort="Hornyak, G L" uniqKey="Hornyak G" first="G. L." last="Hornyak">G. L. Hornyak</name></region><name sortKey="Dillon, A C" sort="Dillon, A C" uniqKey="Dillon A" first="A. C." last="Dillon">A. C. Dillon</name><name sortKey="Fasoon, F S" sort="Fasoon, F S" uniqKey="Fasoon F" first="F. S." last="Fasoon">F. S. Fasoon</name><name sortKey="Heben, M J" sort="Heben, M J" uniqKey="Heben M" first="M. J." last="Heben">M. J. Heben</name><name sortKey="Jones, K M" sort="Jones, K M" uniqKey="Jones K" first="K. M." last="Jones">K. M. Jones</name><name sortKey="Mason, A" sort="Mason, A" uniqKey="Mason A" first="A." last="Mason">A. Mason</name><name sortKey="Parilla, P A" sort="Parilla, P A" uniqKey="Parilla P" first="P. A." last="Parilla">P. A. Parilla</name></country><country name="Allemagne"><noRegion><name sortKey="Schneider, J J" sort="Schneider, J J" uniqKey="Schneider J" first="J. J." last="Schneider">J. J. Schneider</name></noRegion><name sortKey="Czap, N" sort="Czap, N" uniqKey="Czap N" first="N." last="Czap">N. Czap</name></country></tree></affiliations></record>Pour manipuler ce document sous Unix (Dilib)
EXPLOR_STEP=$WICRI_ROOT/Wicri/Terre/explor/CobaltMaghrebV1/Data/Main/Exploration
HfdSelect -h $EXPLOR_STEP/biblio.hfd -nk 000D82 | SxmlIndent | more
Ou
HfdSelect -h $EXPLOR_AREA/Data/Main/Exploration/biblio.hfd -nk 000D82 | SxmlIndent | more
Pour mettre un lien sur cette page dans le réseau Wicri
{{Explor lien
|wiki= Wicri/Terre
|area= CobaltMaghrebV1
|flux= Main
|étape= Exploration
|type= RBID
|clé= ISTEX:DFCCF840DD830F7B0FE1317D587FA0B9FBF5A8D1
|texte= Template synthesis of carbon nanotubes
}}
| This area was generated with Dilib version V0.6.32. |  |