Synthesis, crystal structure and magnetic properties of a new fluoride carbonate Ba2Co(CO3)2F2
Identifieur interne : 000256 ( PascalFrancis/Corpus ); précédent : 000255; suivant : 000257Synthesis, crystal structure and magnetic properties of a new fluoride carbonate Ba2Co(CO3)2F2
Auteurs : A. Ben Ali ; V. Maisonneuve ; S. Kodjikian ; L. S. Smiri ; M. LeblancSource :
- Solid state sciences [ 1293-2558 ] ; 2002.
Descripteurs français
- Pascal (Inist)
English descriptors
- KwdEn :
Abstract
The structure of Ba2Co(CO3)2F2, obtained by hydrothermal synthesis, is determined from X-ray single crystal diffraction data (1085 unique reflections, R = 0.034, RW = 0.078). Ba2Co(CO3)2F2 is orthorhombic, space group Pbca (Z = 4), with a = 6.6226(6), b = 11.494(2), c = 9.021(2) Å and V = 686.7(4) Å3. It can be described from infinite (010) layers of [CoO4F2] octahedra and CO2-3 entities or from [BaO3F]∞ sheets of [BaO7F3] polyhedra. Antiferromagnetic order occurs below TN 6 K.
Notice en format standard (ISO 2709)
Pour connaître la documentation sur le format Inist Standard.
pA |
|
---|
Format Inist (serveur)
NO : | PASCAL 02-0230687 INIST |
---|---|
ET : | Synthesis, crystal structure and magnetic properties of a new fluoride carbonate Ba2Co(CO3)2F2 |
AU : | BEN ALI (A.); MAISONNEUVE (V.); KODJIKIAN (S.); SMIRI (L. S.); LEBLANC (M.) |
AF : | Laboratoire des Fluorures, UMR 6010 CNRS, Faculté des Sciences, Université du Maine, avenue O. Messiaen/72085 Le Mans/France (1 aut., 2 aut., 3 aut., 5 aut.); Laboratoire de Chimie Inorganique et Structurale, Faculté des Sciences de Bizerte/7021 Jarzouna/Tunisie (4 aut.) |
DT : | Publication en série; Niveau analytique |
SO : | Solid state sciences; ISSN 1293-2558; France; Da. 2002; Vol. 4; No. 4; Pp. 503-506; Bibl. 13 ref. |
LA : | Anglais |
EA : | The structure of Ba2Co(CO3)2F2, obtained by hydrothermal synthesis, is determined from X-ray single crystal diffraction data (1085 unique reflections, R = 0.034, RW = 0.078). Ba2Co(CO3)2F2 is orthorhombic, space group Pbca (Z = 4), with a = 6.6226(6), b = 11.494(2), c = 9.021(2) Å and V = 686.7(4) Å3. It can be described from infinite (010) layers of [CoO4F2] octahedra and CO2-3 entities or from [BaO3F]∞ sheets of [BaO7F3] polyhedra. Antiferromagnetic order occurs below TN 6 K. |
CC : | 001B60A66F4; 001B70E30C |
FD : | Etude expérimentale; Préparation chimique; Synthèse hydrothermale; Diffraction RX; Structure cristalline; Susceptibilité magnétique; Aimantation; Antiferromagnétisme; Baryum composé; Cobalt composé; 6166F; 7530C; Ba2Co(CO3)2F2; Ba C Co F O; Fluorocarbonate |
FG : | Fluorure; Carbonate; Composé minéral; Métal transition composé |
ED : | Experimental study; Chemical preparation; Hydrothermal synthesis; XRD; Crystal structure; Magnetic susceptibility; Magnetization; Antiferromagnetism; Barium compounds; Cobalt compounds; Fluorocarbonates |
EG : | Fluorides; Carbonates; Inorganic compounds; Transition element compounds |
LO : | INIST-11118.354000100892180100 |
ID : | 02-0230687 |
Links to Exploration step
Pascal:02-0230687Le document en format XML
<record><TEI><teiHeader><fileDesc><titleStmt><title xml:lang="en" level="a">Synthesis, crystal structure and magnetic properties of a new fluoride carbonate Ba<sub>2</sub>
Co(CO<sub>3</sub>
)<sub>2</sub>
F<sub>2</sub>
</title>
<author><name sortKey="Ben Ali, A" sort="Ben Ali, A" uniqKey="Ben Ali A" first="A." last="Ben Ali">A. Ben Ali</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire des Fluorures, UMR 6010 CNRS, Faculté des Sciences, Université du Maine, avenue O. Messiaen</s1>
<s2>72085 Le Mans</s2>
<s3>FRA</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Maisonneuve, V" sort="Maisonneuve, V" uniqKey="Maisonneuve V" first="V." last="Maisonneuve">V. Maisonneuve</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire des Fluorures, UMR 6010 CNRS, Faculté des Sciences, Université du Maine, avenue O. Messiaen</s1>
<s2>72085 Le Mans</s2>
<s3>FRA</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Kodjikian, S" sort="Kodjikian, S" uniqKey="Kodjikian S" first="S." last="Kodjikian">S. Kodjikian</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire des Fluorures, UMR 6010 CNRS, Faculté des Sciences, Université du Maine, avenue O. Messiaen</s1>
<s2>72085 Le Mans</s2>
<s3>FRA</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Smiri, L S" sort="Smiri, L S" uniqKey="Smiri L" first="L. S." last="Smiri">L. S. Smiri</name>
<affiliation><inist:fA14 i1="02"><s1>Laboratoire de Chimie Inorganique et Structurale, Faculté des Sciences de Bizerte</s1>
<s2>7021 Jarzouna</s2>
<s3>TUN</s3>
<sZ>4 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Leblanc, M" sort="Leblanc, M" uniqKey="Leblanc M" first="M." last="Leblanc">M. Leblanc</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire des Fluorures, UMR 6010 CNRS, Faculté des Sciences, Université du Maine, avenue O. Messiaen</s1>
<s2>72085 Le Mans</s2>
<s3>FRA</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
</titleStmt>
<publicationStmt><idno type="wicri:source">INIST</idno>
<idno type="inist">02-0230687</idno>
<date when="2002">2002</date>
<idno type="stanalyst">PASCAL 02-0230687 INIST</idno>
<idno type="RBID">Pascal:02-0230687</idno>
<idno type="wicri:Area/PascalFrancis/Corpus">000256</idno>
</publicationStmt>
<sourceDesc><biblStruct><analytic><title xml:lang="en" level="a">Synthesis, crystal structure and magnetic properties of a new fluoride carbonate Ba<sub>2</sub>
Co(CO<sub>3</sub>
)<sub>2</sub>
F<sub>2</sub>
</title>
<author><name sortKey="Ben Ali, A" sort="Ben Ali, A" uniqKey="Ben Ali A" first="A." last="Ben Ali">A. Ben Ali</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire des Fluorures, UMR 6010 CNRS, Faculté des Sciences, Université du Maine, avenue O. Messiaen</s1>
<s2>72085 Le Mans</s2>
<s3>FRA</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Maisonneuve, V" sort="Maisonneuve, V" uniqKey="Maisonneuve V" first="V." last="Maisonneuve">V. Maisonneuve</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire des Fluorures, UMR 6010 CNRS, Faculté des Sciences, Université du Maine, avenue O. Messiaen</s1>
<s2>72085 Le Mans</s2>
<s3>FRA</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Kodjikian, S" sort="Kodjikian, S" uniqKey="Kodjikian S" first="S." last="Kodjikian">S. Kodjikian</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire des Fluorures, UMR 6010 CNRS, Faculté des Sciences, Université du Maine, avenue O. Messiaen</s1>
<s2>72085 Le Mans</s2>
<s3>FRA</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Smiri, L S" sort="Smiri, L S" uniqKey="Smiri L" first="L. S." last="Smiri">L. S. Smiri</name>
<affiliation><inist:fA14 i1="02"><s1>Laboratoire de Chimie Inorganique et Structurale, Faculté des Sciences de Bizerte</s1>
<s2>7021 Jarzouna</s2>
<s3>TUN</s3>
<sZ>4 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
<author><name sortKey="Leblanc, M" sort="Leblanc, M" uniqKey="Leblanc M" first="M." last="Leblanc">M. Leblanc</name>
<affiliation><inist:fA14 i1="01"><s1>Laboratoire des Fluorures, UMR 6010 CNRS, Faculté des Sciences, Université du Maine, avenue O. Messiaen</s1>
<s2>72085 Le Mans</s2>
<s3>FRA</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</inist:fA14>
</affiliation>
</author>
</analytic>
<series><title level="j" type="main">Solid state sciences</title>
<title level="j" type="abbreviated">Solid state sci.</title>
<idno type="ISSN">1293-2558</idno>
<imprint><date when="2002">2002</date>
</imprint>
</series>
</biblStruct>
</sourceDesc>
<seriesStmt><title level="j" type="main">Solid state sciences</title>
<title level="j" type="abbreviated">Solid state sci.</title>
<idno type="ISSN">1293-2558</idno>
</seriesStmt>
</fileDesc>
<profileDesc><textClass><keywords scheme="KwdEn" xml:lang="en"><term>Antiferromagnetism</term>
<term>Barium compounds</term>
<term>Chemical preparation</term>
<term>Cobalt compounds</term>
<term>Crystal structure</term>
<term>Experimental study</term>
<term>Fluorocarbonates</term>
<term>Hydrothermal synthesis</term>
<term>Magnetic susceptibility</term>
<term>Magnetization</term>
<term>XRD</term>
</keywords>
<keywords scheme="Pascal" xml:lang="fr"><term>Etude expérimentale</term>
<term>Préparation chimique</term>
<term>Synthèse hydrothermale</term>
<term>Diffraction RX</term>
<term>Structure cristalline</term>
<term>Susceptibilité magnétique</term>
<term>Aimantation</term>
<term>Antiferromagnétisme</term>
<term>Baryum composé</term>
<term>Cobalt composé</term>
<term>6166F</term>
<term>7530C</term>
<term>Ba2Co(CO3)2F2</term>
<term>Ba C Co F O</term>
<term>Fluorocarbonate</term>
</keywords>
</textClass>
</profileDesc>
</teiHeader>
<front><div type="abstract" xml:lang="en">The structure of Ba<sub>2</sub>
Co(CO<sub>3</sub>
)<sub>2</sub>
F<sub>2</sub>
, obtained by hydrothermal synthesis, is determined from X-ray single crystal diffraction data (1085 unique reflections, R = 0.034, R<sub>W</sub>
= 0.078). Ba<sub>2</sub>
Co(CO<sub>3</sub>
)<sub>2</sub>
F<sub>2</sub>
is orthorhombic, space group Pbca (Z = 4), with a = 6.6226(6), b = 11.494(2), c = 9.021(2) Å and V = 686.7(4) Å<sup>3</sup>
. It can be described from infinite (010) layers of [CoO<sub>4</sub>
F<sub>2</sub>
] octahedra and CO<sup>2-</sup>
<sub>3</sub>
entities or from [BaO<sub>3</sub>
F]∞ sheets of [BaO<sub>7</sub>
F<sub>3</sub>
] polyhedra. Antiferromagnetic order occurs below T<sub>N</sub>
6 K.</div>
</front>
</TEI>
<inist><standard h6="B"><pA><fA01 i1="01" i2="1"><s0>1293-2558</s0>
</fA01>
<fA03 i2="1"><s0>Solid state sci.</s0>
</fA03>
<fA05><s2>4</s2>
</fA05>
<fA06><s2>4</s2>
</fA06>
<fA08 i1="01" i2="1" l="ENG"><s1>Synthesis, crystal structure and magnetic properties of a new fluoride carbonate Ba<sub>2</sub>
Co(CO<sub>3</sub>
)<sub>2</sub>
F<sub>2</sub>
</s1>
</fA08>
<fA11 i1="01" i2="1"><s1>BEN ALI (A.)</s1>
</fA11>
<fA11 i1="02" i2="1"><s1>MAISONNEUVE (V.)</s1>
</fA11>
<fA11 i1="03" i2="1"><s1>KODJIKIAN (S.)</s1>
</fA11>
<fA11 i1="04" i2="1"><s1>SMIRI (L. S.)</s1>
</fA11>
<fA11 i1="05" i2="1"><s1>LEBLANC (M.)</s1>
</fA11>
<fA14 i1="01"><s1>Laboratoire des Fluorures, UMR 6010 CNRS, Faculté des Sciences, Université du Maine, avenue O. Messiaen</s1>
<s2>72085 Le Mans</s2>
<s3>FRA</s3>
<sZ>1 aut.</sZ>
<sZ>2 aut.</sZ>
<sZ>3 aut.</sZ>
<sZ>5 aut.</sZ>
</fA14>
<fA14 i1="02"><s1>Laboratoire de Chimie Inorganique et Structurale, Faculté des Sciences de Bizerte</s1>
<s2>7021 Jarzouna</s2>
<s3>TUN</s3>
<sZ>4 aut.</sZ>
</fA14>
<fA20><s1>503-506</s1>
</fA20>
<fA21><s1>2002</s1>
</fA21>
<fA23 i1="01"><s0>ENG</s0>
</fA23>
<fA43 i1="01"><s1>INIST</s1>
<s2>11118</s2>
<s5>354000100892180100</s5>
</fA43>
<fA44><s0>0000</s0>
<s1>© 2002 INIST-CNRS. All rights reserved.</s1>
</fA44>
<fA45><s0>13 ref.</s0>
</fA45>
<fA47 i1="01" i2="1"><s0>02-0230687</s0>
</fA47>
<fA60><s1>P</s1>
</fA60>
<fA61><s0>A</s0>
</fA61>
<fA64 i1="01" i2="1"><s0>Solid state sciences</s0>
</fA64>
<fA66 i1="01"><s0>FRA</s0>
</fA66>
<fC01 i1="01" l="ENG"><s0>The structure of Ba<sub>2</sub>
Co(CO<sub>3</sub>
)<sub>2</sub>
F<sub>2</sub>
, obtained by hydrothermal synthesis, is determined from X-ray single crystal diffraction data (1085 unique reflections, R = 0.034, R<sub>W</sub>
= 0.078). Ba<sub>2</sub>
Co(CO<sub>3</sub>
)<sub>2</sub>
F<sub>2</sub>
is orthorhombic, space group Pbca (Z = 4), with a = 6.6226(6), b = 11.494(2), c = 9.021(2) Å and V = 686.7(4) Å<sup>3</sup>
. It can be described from infinite (010) layers of [CoO<sub>4</sub>
F<sub>2</sub>
] octahedra and CO<sup>2-</sup>
<sub>3</sub>
entities or from [BaO<sub>3</sub>
F]∞ sheets of [BaO<sub>7</sub>
F<sub>3</sub>
] polyhedra. Antiferromagnetic order occurs below T<sub>N</sub>
6 K.</s0>
</fC01>
<fC02 i1="01" i2="3"><s0>001B60A66F4</s0>
</fC02>
<fC02 i1="02" i2="3"><s0>001B70E30C</s0>
</fC02>
<fC03 i1="01" i2="3" l="FRE"><s0>Etude expérimentale</s0>
<s5>01</s5>
</fC03>
<fC03 i1="01" i2="3" l="ENG"><s0>Experimental study</s0>
<s5>01</s5>
</fC03>
<fC03 i1="02" i2="3" l="FRE"><s0>Préparation chimique</s0>
<s5>02</s5>
</fC03>
<fC03 i1="02" i2="3" l="ENG"><s0>Chemical preparation</s0>
<s5>02</s5>
</fC03>
<fC03 i1="03" i2="3" l="FRE"><s0>Synthèse hydrothermale</s0>
<s5>03</s5>
</fC03>
<fC03 i1="03" i2="3" l="ENG"><s0>Hydrothermal synthesis</s0>
<s5>03</s5>
</fC03>
<fC03 i1="04" i2="3" l="FRE"><s0>Diffraction RX</s0>
<s5>05</s5>
</fC03>
<fC03 i1="04" i2="3" l="ENG"><s0>XRD</s0>
<s5>05</s5>
</fC03>
<fC03 i1="05" i2="3" l="FRE"><s0>Structure cristalline</s0>
<s5>06</s5>
</fC03>
<fC03 i1="05" i2="3" l="ENG"><s0>Crystal structure</s0>
<s5>06</s5>
</fC03>
<fC03 i1="06" i2="3" l="FRE"><s0>Susceptibilité magnétique</s0>
<s5>07</s5>
</fC03>
<fC03 i1="06" i2="3" l="ENG"><s0>Magnetic susceptibility</s0>
<s5>07</s5>
</fC03>
<fC03 i1="07" i2="3" l="FRE"><s0>Aimantation</s0>
<s5>08</s5>
</fC03>
<fC03 i1="07" i2="3" l="ENG"><s0>Magnetization</s0>
<s5>08</s5>
</fC03>
<fC03 i1="08" i2="3" l="FRE"><s0>Antiferromagnétisme</s0>
<s5>09</s5>
</fC03>
<fC03 i1="08" i2="3" l="ENG"><s0>Antiferromagnetism</s0>
<s5>09</s5>
</fC03>
<fC03 i1="09" i2="3" l="FRE"><s0>Baryum composé</s0>
<s5>11</s5>
</fC03>
<fC03 i1="09" i2="3" l="ENG"><s0>Barium compounds</s0>
<s5>11</s5>
</fC03>
<fC03 i1="10" i2="3" l="FRE"><s0>Cobalt composé</s0>
<s5>12</s5>
</fC03>
<fC03 i1="10" i2="3" l="ENG"><s0>Cobalt compounds</s0>
<s5>12</s5>
</fC03>
<fC03 i1="11" i2="3" l="FRE"><s0>6166F</s0>
<s2>PAC</s2>
<s4>INC</s4>
<s5>56</s5>
</fC03>
<fC03 i1="12" i2="3" l="FRE"><s0>7530C</s0>
<s2>PAC</s2>
<s4>INC</s4>
<s5>57</s5>
</fC03>
<fC03 i1="13" i2="3" l="FRE"><s0>Ba2Co(CO3)2F2</s0>
<s4>INC</s4>
<s5>94</s5>
</fC03>
<fC03 i1="14" i2="3" l="FRE"><s0>Ba C Co F O</s0>
<s4>INC</s4>
<s5>95</s5>
</fC03>
<fC03 i1="15" i2="3" l="FRE"><s0>Fluorocarbonate</s0>
<s4>CD</s4>
<s5>96</s5>
</fC03>
<fC03 i1="15" i2="3" l="ENG"><s0>Fluorocarbonates</s0>
<s4>CD</s4>
<s5>96</s5>
</fC03>
<fC07 i1="01" i2="3" l="FRE"><s0>Fluorure</s0>
<s2>NA</s2>
<s5>16</s5>
</fC07>
<fC07 i1="01" i2="3" l="ENG"><s0>Fluorides</s0>
<s2>NA</s2>
<s5>16</s5>
</fC07>
<fC07 i1="02" i2="3" l="FRE"><s0>Carbonate</s0>
<s2>NA</s2>
<s5>17</s5>
</fC07>
<fC07 i1="02" i2="3" l="ENG"><s0>Carbonates</s0>
<s2>NA</s2>
<s5>17</s5>
</fC07>
<fC07 i1="03" i2="3" l="FRE"><s0>Composé minéral</s0>
<s5>18</s5>
</fC07>
<fC07 i1="03" i2="3" l="ENG"><s0>Inorganic compounds</s0>
<s5>18</s5>
</fC07>
<fC07 i1="04" i2="3" l="FRE"><s0>Métal transition composé</s0>
<s5>81</s5>
</fC07>
<fC07 i1="04" i2="3" l="ENG"><s0>Transition element compounds</s0>
<s5>81</s5>
</fC07>
<fN21><s1>140</s1>
</fN21>
<fN82><s1>PSI</s1>
</fN82>
</pA>
</standard>
<server><NO>PASCAL 02-0230687 INIST</NO>
<ET>Synthesis, crystal structure and magnetic properties of a new fluoride carbonate Ba<sub>2</sub>
Co(CO<sub>3</sub>
)<sub>2</sub>
F<sub>2</sub>
</ET>
<AU>BEN ALI (A.); MAISONNEUVE (V.); KODJIKIAN (S.); SMIRI (L. S.); LEBLANC (M.)</AU>
<AF>Laboratoire des Fluorures, UMR 6010 CNRS, Faculté des Sciences, Université du Maine, avenue O. Messiaen/72085 Le Mans/France (1 aut., 2 aut., 3 aut., 5 aut.); Laboratoire de Chimie Inorganique et Structurale, Faculté des Sciences de Bizerte/7021 Jarzouna/Tunisie (4 aut.)</AF>
<DT>Publication en série; Niveau analytique</DT>
<SO>Solid state sciences; ISSN 1293-2558; France; Da. 2002; Vol. 4; No. 4; Pp. 503-506; Bibl. 13 ref.</SO>
<LA>Anglais</LA>
<EA>The structure of Ba<sub>2</sub>
Co(CO<sub>3</sub>
)<sub>2</sub>
F<sub>2</sub>
, obtained by hydrothermal synthesis, is determined from X-ray single crystal diffraction data (1085 unique reflections, R = 0.034, R<sub>W</sub>
= 0.078). Ba<sub>2</sub>
Co(CO<sub>3</sub>
)<sub>2</sub>
F<sub>2</sub>
is orthorhombic, space group Pbca (Z = 4), with a = 6.6226(6), b = 11.494(2), c = 9.021(2) Å and V = 686.7(4) Å<sup>3</sup>
. It can be described from infinite (010) layers of [CoO<sub>4</sub>
F<sub>2</sub>
] octahedra and CO<sup>2-</sup>
<sub>3</sub>
entities or from [BaO<sub>3</sub>
F]∞ sheets of [BaO<sub>7</sub>
F<sub>3</sub>
] polyhedra. Antiferromagnetic order occurs below T<sub>N</sub>
6 K.</EA>
<CC>001B60A66F4; 001B70E30C</CC>
<FD>Etude expérimentale; Préparation chimique; Synthèse hydrothermale; Diffraction RX; Structure cristalline; Susceptibilité magnétique; Aimantation; Antiferromagnétisme; Baryum composé; Cobalt composé; 6166F; 7530C; Ba2Co(CO3)2F2; Ba C Co F O; Fluorocarbonate</FD>
<FG>Fluorure; Carbonate; Composé minéral; Métal transition composé</FG>
<ED>Experimental study; Chemical preparation; Hydrothermal synthesis; XRD; Crystal structure; Magnetic susceptibility; Magnetization; Antiferromagnetism; Barium compounds; Cobalt compounds; Fluorocarbonates</ED>
<EG>Fluorides; Carbonates; Inorganic compounds; Transition element compounds</EG>
<LO>INIST-11118.354000100892180100</LO>
<ID>02-0230687</ID>
</server>
</inist>
</record>
Pour manipuler ce document sous Unix (Dilib)
EXPLOR_STEP=$WICRI_ROOT/Wicri/Terre/explor/CobaltMaghrebV1/Data/PascalFrancis/Corpus
HfdSelect -h $EXPLOR_STEP/biblio.hfd -nk 000256 | SxmlIndent | more
Ou
HfdSelect -h $EXPLOR_AREA/Data/PascalFrancis/Corpus/biblio.hfd -nk 000256 | SxmlIndent | more
Pour mettre un lien sur cette page dans le réseau Wicri
{{Explor lien |wiki= Wicri/Terre |area= CobaltMaghrebV1 |flux= PascalFrancis |étape= Corpus |type= RBID |clé= Pascal:02-0230687 |texte= Synthesis, crystal structure and magnetic properties of a new fluoride carbonate Ba2Co(CO3)2F2 }}
This area was generated with Dilib version V0.6.32. |