Analysis of fatigue crack growth in a rubber-toughened epoxy resin: effect of temperature and stress ratio
Identifieur interne : 003189 ( Main/Merge ); précédent : 003188; suivant : 003190Analysis of fatigue crack growth in a rubber-toughened epoxy resin: effect of temperature and stress ratio
Auteurs : Moustafa Abou-Hamda [Australie] ; Yiu-Wing Mai [Australie] ; Shang-Xian Wu [Australie] ; Brian Cotterell [Singapour]Source :
- Polymer [ 0032-3861 ] ; 1992.
Abstract
Fatigue crack propagation in a rubber-toughened epoxy resin was studied at different test temperatures (−40 to 60°C) and stress ratios (0.05 to 0.70) using single edge-notched specimens at a frequency of 5 Hz. Fatigue crack propagation rates (dadN) were plotted against the stress-intensity factor amplitude (ΔK) in accordance with the Paris power-law equation. For a given stress ratio dadN was not sensitive to variations in test temperature. But for a given temperature dadN increased with stress ratio. Using the Williams' two-stage line zone model to analyse these experimental data, it was shown that the main failure process was due to shear plastic flow at the crack tip. The fatigue stress and the closure stress-intensity factor both decreased with increasing temperature, implying that more severe damage had occurred at higher testing temperatures. The experimental data were also analysed in terms of a new fatigue model, which considers the accumulation of damage due to cyclic plastic strain in the reversed plastic zone similar to the Coffin-Manson law and crack closure due to residual plastic stretch at the crack wake. There was good agreement between theory and experiment, suggesting a simpler way to correlate fatigue crack growth rates in this and other polymeric materials.
Url:
DOI: 10.1016/0032-3861(93)90180-I
Links toward previous steps (curation, corpus...)
- to stream Istex, to step Corpus: 001790
- to stream Istex, to step Curation: 001692
- to stream Istex, to step Checkpoint: 002278
Links to Exploration step
ISTEX:89259FEC07DDA00B9DD72C271411C6375C312DAELe document en format XML
<record><TEI wicri:istexFullTextTei="biblStruct"><teiHeader><fileDesc><titleStmt><title>Analysis of fatigue crack growth in a rubber-toughened epoxy resin: effect of temperature and stress ratio</title>
<author><name sortKey="Abou Hamda, Moustafa" sort="Abou Hamda, Moustafa" uniqKey="Abou Hamda M" first="Moustafa" last="Abou-Hamda">Moustafa Abou-Hamda</name>
</author>
<author><name sortKey="Mai, Yiu Wing" sort="Mai, Yiu Wing" uniqKey="Mai Y" first="Yiu-Wing" last="Mai">Yiu-Wing Mai</name>
</author>
<author><name sortKey="Wu, Shang Xian" sort="Wu, Shang Xian" uniqKey="Wu S" first="Shang-Xian" last="Wu">Shang-Xian Wu</name>
</author>
<author><name sortKey="Cotterell, Brian" sort="Cotterell, Brian" uniqKey="Cotterell B" first="Brian" last="Cotterell">Brian Cotterell</name>
</author>
</titleStmt>
<publicationStmt><idno type="wicri:source">ISTEX</idno>
<idno type="RBID">ISTEX:89259FEC07DDA00B9DD72C271411C6375C312DAE</idno>
<date when="1993" year="1993">1993</date>
<idno type="doi">10.1016/0032-3861(93)90180-I</idno>
<idno type="url">https://api.istex.fr/document/89259FEC07DDA00B9DD72C271411C6375C312DAE/fulltext/pdf</idno>
<idno type="wicri:Area/Istex/Corpus">001790</idno>
<idno type="wicri:Area/Istex/Curation">001692</idno>
<idno type="wicri:Area/Istex/Checkpoint">002278</idno>
<idno type="wicri:doubleKey">0032-3861:1993:Abou Hamda M:analysis:of:fatigue</idno>
<idno type="wicri:Area/Main/Merge">003189</idno>
</publicationStmt>
<sourceDesc><biblStruct><analytic><title level="a">Analysis of fatigue crack growth in a rubber-toughened epoxy resin: effect of temperature and stress ratio</title>
<author><name sortKey="Abou Hamda, Moustafa" sort="Abou Hamda, Moustafa" uniqKey="Abou Hamda M" first="Moustafa" last="Abou-Hamda">Moustafa Abou-Hamda</name>
<affiliation wicri:level="1"><country xml:lang="fr">Australie</country>
<wicri:regionArea>Centre for Advanced Materials Technology, Department of Mechanical Engineering, University of Sydney, New South Wales 2006</wicri:regionArea>
<wicri:noRegion>New South Wales 2006</wicri:noRegion>
</affiliation>
</author>
<author><name sortKey="Mai, Yiu Wing" sort="Mai, Yiu Wing" uniqKey="Mai Y" first="Yiu-Wing" last="Mai">Yiu-Wing Mai</name>
<affiliation wicri:level="1"><country xml:lang="fr">Australie</country>
<wicri:regionArea>Centre for Advanced Materials Technology, Department of Mechanical Engineering, University of Sydney, New South Wales 2006</wicri:regionArea>
<wicri:noRegion>New South Wales 2006</wicri:noRegion>
</affiliation>
</author>
<author><name sortKey="Wu, Shang Xian" sort="Wu, Shang Xian" uniqKey="Wu S" first="Shang-Xian" last="Wu">Shang-Xian Wu</name>
<affiliation wicri:level="1"><country xml:lang="fr">Australie</country>
<wicri:regionArea>Centre for Advanced Materials Technology, Department of Mechanical Engineering, University of Sydney, New South Wales 2006</wicri:regionArea>
<wicri:noRegion>New South Wales 2006</wicri:noRegion>
</affiliation>
</author>
<author><name sortKey="Cotterell, Brian" sort="Cotterell, Brian" uniqKey="Cotterell B" first="Brian" last="Cotterell">Brian Cotterell</name>
<affiliation wicri:level="4"><country xml:lang="fr">Singapour</country>
<wicri:regionArea>School of Mechanical and Production Engineering, National University of Singapore</wicri:regionArea>
<orgName type="university">Université nationale de Singapour</orgName>
</affiliation>
</author>
</analytic>
<monogr></monogr>
<series><title level="j">Polymer</title>
<title level="j" type="abbrev">JPOL</title>
<idno type="ISSN">0032-3861</idno>
<imprint><publisher>ELSEVIER</publisher>
<date type="published" when="1992">1992</date>
<biblScope unit="volume">34</biblScope>
<biblScope unit="issue">20</biblScope>
<biblScope unit="page" from="4221">4221</biblScope>
<biblScope unit="page" to="4229">4229</biblScope>
</imprint>
<idno type="ISSN">0032-3861</idno>
</series>
<idno type="istex">89259FEC07DDA00B9DD72C271411C6375C312DAE</idno>
<idno type="DOI">10.1016/0032-3861(93)90180-I</idno>
<idno type="PII">0032-3861(93)90180-I</idno>
</biblStruct>
</sourceDesc>
<seriesStmt><idno type="ISSN">0032-3861</idno>
</seriesStmt>
</fileDesc>
<profileDesc><textClass></textClass>
<langUsage><language ident="en">en</language>
</langUsage>
</profileDesc>
</teiHeader>
<front><div type="abstract" xml:lang="en">Fatigue crack propagation in a rubber-toughened epoxy resin was studied at different test temperatures (−40 to 60°C) and stress ratios (0.05 to 0.70) using single edge-notched specimens at a frequency of 5 Hz. Fatigue crack propagation rates (dadN) were plotted against the stress-intensity factor amplitude (ΔK) in accordance with the Paris power-law equation. For a given stress ratio dadN was not sensitive to variations in test temperature. But for a given temperature dadN increased with stress ratio. Using the Williams' two-stage line zone model to analyse these experimental data, it was shown that the main failure process was due to shear plastic flow at the crack tip. The fatigue stress and the closure stress-intensity factor both decreased with increasing temperature, implying that more severe damage had occurred at higher testing temperatures. The experimental data were also analysed in terms of a new fatigue model, which considers the accumulation of damage due to cyclic plastic strain in the reversed plastic zone similar to the Coffin-Manson law and crack closure due to residual plastic stretch at the crack wake. There was good agreement between theory and experiment, suggesting a simpler way to correlate fatigue crack growth rates in this and other polymeric materials.</div>
</front>
</TEI>
</record>
Pour manipuler ce document sous Unix (Dilib)
EXPLOR_STEP=$WICRI_ROOT/Ticri/CIDE/explor/OcrV1/Data/Main/Merge
HfdSelect -h $EXPLOR_STEP/biblio.hfd -nk 003189 | SxmlIndent | more
Ou
HfdSelect -h $EXPLOR_AREA/Data/Main/Merge/biblio.hfd -nk 003189 | SxmlIndent | more
Pour mettre un lien sur cette page dans le réseau Wicri
{{Explor lien |wiki= Ticri/CIDE |area= OcrV1 |flux= Main |étape= Merge |type= RBID |clé= ISTEX:89259FEC07DDA00B9DD72C271411C6375C312DAE |texte= Analysis of fatigue crack growth in a rubber-toughened epoxy resin: effect of temperature and stress ratio }}
This area was generated with Dilib version V0.6.32. |